N-thiocarbamoyl-polyalkylenepolyamine group containing heavy metal adsorbing resins

ABSTRACT

A heavy metal adsorbing resin of which the main polymer chain consists of an aliphatic hydrocarbon skeleton and which contains at least one functional group selected from amino, polyalkylene polyamino, hydrazido, thioureido, thiosemicarbazido, isothiocyanato, thiobiuret, N-thioaminobiuret, and Nthiocarbamoyl-polyalkylene amino groups. Heavy metals can be removed from a solution containing them by contacting the solution with the above heavy metal adsorbing resin. The resin has a markedly high rate of adsorbing the heavy metals, and can be easily regenerated with a mineral acid or sodium sulfide. The suitable time of regenerating or replacing the resin can be detected by its color change upon adsorption of the heavy metals.

United States Patent 1 Motani et al.

[4 1 July 1, 1975 RESINS [75] Inventors: Kensuke Motani; Akihiko Nakahara; Nobuyuki Kuramoto, all of Tokuyama, Japan [73] Assignee: Tokuyama Soda Kabushiki Kaisha,

Japan [22] Filed: May 30,1974

21 App1.N0.:474,723

Related U.S. Application Data [62] Division of Ser. No. 339,382, March 7, 1973, Pat.

[30] Foreign Application Priority Data Mar. 11, 1972 Japan 47-24424 Mar. 11, 1972 Japan... 47-24425 Mar. 11, 1972 Japan... 47-24426 Mar. 11, 1972 Japan 47-24427 [56] References Cited UNITED STATES PATENTS 2,890,180 6/1959 Cerny et al. 260/21 3,196,107 7/1965 Tomic 210/38 3,473,921 10/1969 Schmuckler 75/1 18 3,687,908 8/1972 Pickleshimer 260/795 OTHER PUBLICATIONS Campbell et al., J. Polym. Sci. 62, 379-86( 1962).

Primary ExaminerMelvin Goldstein Attorney, Agent, or FirmSherman & Shalloway [5 7 ABSTRACT A heavy metal adsorbing resin of which the main polymer chain consists of an aliphatic hydrocarbon skeleton and which contains at least one functional group selected from amino, polyalkylene polyamino, hydrazido, thioureido, thiosemicarbazido, isothiocyanato, thiobiuret, N-thioaminobiuret, and N-thiocarbamoyl-polyalkylene amino groups. Heavy metals can be removed from a solution containing them by contacting the solution with the above heavy metal adsorbing resin. The resin has a markedly high rate of adsorbing the heavy metals, and can be easily regenerated with a mineral acid or sodium sulfide. The suitable time of regenerating or replacing the resin can be detected by its color change upon adsorption of the heavy metals.

2 Claims, N0 Drawings N-THIOCARBAMOYL- POLYALKYLENEPOLYAMINE GROUP CONTAINING HEAVY METAL ADSORBING RESINS This is a division of application Ser. No. 339,382, filed Mar. 7, 1973, now US. Pat. No. 3,847,84l.

This invention relates to a resin having the property of adsorbing heavy metals. More specifically, it relates to a heavy metal adsorbing resin of which the main chain consists of an aliphatic hydrocarbon skeleton and which contains at least onefunctional group selected from the group consisting of amino, polyalkylene polyamino, hydrazido, thioureido, thiosemicarbazido, isothiocyanato, thiobiuret, N-thioaminobiruet and N-thiocarbamoylpolyalkylene amino groups.

Methods have previously been known to remove heavy metals such as mercury from a solution containing them by causing an anion exchange resin to adsorb them. However, these methods are commercially infeasible because of the defect that not only the exchange resin has poor ability to adsorb heavy metals, but also the solution treated still contains large quantities of the heavy metals.

In recent years, methods have been proposed to adsorb heavy metals using a chelate resin, but almost all of them have not proved satisfactory for industrial application. For example, a condensation-type chelate resin obtained by reacting thiourea, resorcinol and formaldehyde is considered best suited foruse in such a method. However, the condensation-type chelate resin has the defect that its ability to adsorb heavy metals is not entirely satisfactory, its mechanical strength is poor, and it is difficult to regenerate with acid after adsorption of heavy metals.

Accordingly, heavy metal adsorbing resins of better quality have been desired in the art.

An object of this invention is to provide a resin which has a high ability to adsorb heavy metals and high mechanical strength, and which can be easily regenerated.

Another object of this invention is to provide a resin which distinctly discolors upon adsorption of heavy metals.

The othere objects and the advantages of this invention will become apparent from the following description.

According to this invention, there is provided a heavy metal adsorbing resin of which the main chain consists of an aliphatic hydrocarbon skeleton and which contains at least one functional group selected from the group consisting of amino, polyalkylene polyamino, hydrazido, thioureido, thiosemicarbazido, thiocyanato, thiobiuret, Nthioaminobiuret, and N-thiocarbamoylpolyalkylene amino groups.

The heavy metal adsorbing resin of this invention has a markedly high speed of adsorption of heavy metals as compared with the conventional chelate resins, and can adsorb heavy metals almost completely from a solution containing them in low concentrations. Accordingly, when the heavy metal adsorbing resin is contacted with a solution containing heavy metals, the treated solution has very low concentrations of the heavy metals, and the concentrations are constant until the resin has adsorbed the heavy metals and almost reached saturation. Such a characteristic of the heavy metal adsorbing resin of this invention is quite different from that of the conventional condensation-type chelate resin whose contact.

Since the resin of this invention exhibits a clear discoloration upon adsorption of heavy metals, it serves to determine whether the adsorbing ability of the resin has reached saturation. Therefore, one can easily see when the resin of this invention should be regenerated or replaced, and this adds to the commercial advantage of the resin in accordance with the present invention. The resin of this invention can also be used as an expedient for detecting the presence of heavy metals in waste water. The heavy metal adsorbing resin also lends itself to easy handling because of its superior mechanical strength, and is scarcely broken during its regeneration or scarcely lost during its production by granulation. This if, of course, economically advantageous, I

The heavy metal adsorbing resin has the advantage of being able to be regenerated by treatment with an acid after the adsorption of heavy metals to regain its adsorbing ability.

The various advantages of the resin over the conventional chelate resins cannot be ascribed to any clear cause. However, we assume that such advantages are ascribable to the fact that the main chain of the resin consists of an aliphatic hydrocarbon skeleton (the socalled polymerized type high-molecular-weight polymer) and the specific functional group bonded thereto synergistically acts to provide a chelating adsorbing power or other adsorbing power.

The base of the heavy metal adsorbing resin of this invention may be any of which the main chain consists of a polymerized-type high-molecular-weight polymer having a carbon-to-carbon bond and may be a known homopolymer, copolymer or graft copolymer. Typical examples of such polymers than can be suitably used include polymers of olefins such as polyethylene, polypropylene, polybutene, polybutadiene or polyisoprene and copolymers of olefins; copolymers of olefins with other copolymerizable monomers such as vinyl chloride, vinylidene chloride, an acrylic acid ester or a methacrylic acid ester; polymers of unsaturated aliphatic halogenated hydrocarbons such as vinyl chloride, vinylidene chloride, vinylidene chloride or chloroprene; copolymers of the aforesaid unsaturated aliphatic halogenated hydrocarbons with other copolymerizable monomers such as an olefin, vinyl ester, vinyl ether, acrylonitrile, acrylic acid ester or methacrylic acid ester; polymers of acrylonitrile, acrylic acid esters or methacrylic acid esters; polymers of styrene or styrene derivatives; copolymers of the aforesaid styrene monomers with other copolymerizable monomers such as acrylonitrile or a methacrylic acid ester; and graft copolymers obtained by grafting the aforementioned monomers to rubbery substances such as a polyalkylene oxide, polybutadiene, ethylene/propylene copolymer or ethylene/propylene/diene terpolymer. Espe cially when a polymer, copolymer or graft copolymer of the unsaturated aliphatic halogenated hydrocarbon is used as the resin base, the introduction of the functional group is easy, and the resulting heavy metal adsorbing resin exhibits very superior advantages.

It is essential in the present invention that the main chain of the heavy metal adsorbing resin consists of the aliphatic hydrocarbon skeleton, and at least one functional group selected from amino, polyalkylene poly amino, hydrazido, thioureido, thiosemicarbazido, isothiocyanato, thiobiuret, N-thioaminobiuret and N-thiocarbamoyl-polyalkylene polyamino group is directly or indirectly attached to the main chain.

All resins containing the aforementioned functional groups have excellent ability to adsorb heavy metals. Those containing at least one nitrogen-containing functional group selected from amino, hydrazide and polyalkylene polyamino groups have especially high speeds of adsorbing heavy metals, and after contacting them with a heavy metal containing solution, the concentration of the heavy metal remaining in the solution (this concentration will also be referred to simply as a flowthrough value) is on the order of 0.01 ppm when the heavy metal is mercury.

On the other hand, those containing at least one nitrogenand sulfur-containing functional group selected from thioureido, thiosemicarbazido and N-thiocarbamoylpolyalkylene amino groups have a large absorption capacity for heavy metals, and have a flow-through value of less than 0.001 ppm for mercury, which means that the heavy metal is adsorbed and removed almost completely.

Accordingly, heavy metals can be efficiently and economically removed to low concentrations from a solution containing them by first bringing the solution into contact with a chelate resin containing at least one functional group selected from amino, hydrazido and polyalkyleneamino groups, and then with a resin containing at least one functional group selected from thiourea, thiosemicarbazide and N-thiocarbamoylpolyalkylene amino groups.

The functional groups contained in the resin of this invention are expressed by the general formula as follows:

amino groups -NHR polyalkylene polyamino groups -NH[CH CH NH],,.R

hydrazido groups -NHNHR thioureido groups -NHCSNHR isothiocyanato group -NCS thiosemicarbazido groups -NHNHCSNHR (or -NHCSNHNHR) thiobiuret groups -NHCSNHCONHR (or -NHCONHCSNHR) N-thioaminobiuret groups -NHNHCSNHCONHR (or NHNHCONHCSNHR) N-thiocarbamoylpolyalkylene polyamino groups In these formulae, R is a hydrogen atom, alkyl group, aryl group or acyl group, and n is l to 100, preferably 1 to 5.

The number of the functional groups to be attached to the resin base is at least one per molecular of the base. Usually, the number is at least 1 per about 250, preferably 100, monomer units in order to provide suitable heavy metal adsorbing resins of this invention.

The functional group may be bonded to the carbon atom of the main chain of the polymer. When the polymer contains a pendant aliphatic or aromatic group, the functional group may be attached to the carbon atom of the pendant aliphatic or aromatic group.

The method of preparation of the resin of this invention is not particularly limited. Generally, according to the purpose of use of the resulting resin, the functional group is introduced into a granulated base polymer of high molecular weight of which the main chain consists of an aliphatic hydrocarbon skeleton. The size of the granules is 10 to 300 mesh, preferably 15 to 50 mesh.

Below are given some examples of reactions that can be suitably used for producing the heavy metal adsorbing resins of this invention.

1. A hypohydrohalous acid salt is reacted in alkali with a high-molecular-weight polymer (to be referred to simply as a base polymer) of which the main chain consists of an aliphatic hydrocarbon skeleton and which contains a carbamoyl group (-CONH introduced thereinto to produce a heavy metal-adsorbing resin of this invention containing an amino group (the so-called Hofmann degradation).

2. A base polymer having a cyano group (-CN) or nitro group (NO introduced thereinto is reduced with a metal hydride or tin-hydrochloric acid thereby to form a heavy metal adsorbing resin of this invention containing an amino group.

3. A base polymer containing a halogen atom either in itself or introduced thereinto is reacted with ammonia, hydrazine or a polyalkylene polyamine to produce a resin containing an amino group (NH hydrazido group (NHNH or polyalkylene polyamino group [NH(C H ,NH),,H] respectively. In this case, a vinyl chloride polymer or a copolymer or graft copolymer consisting mainly of vinyl chloride units can be suitably used. l I A 4. The above resin containing an amino, hydrazide or polyalkylene polyamino group either as such or after being converted to its hydrochloride, is reacted with'a sulfur-containing compound selected from the group consisting of thiocyanic acid salts, thioureas, carbon disulfide, isothiocyanates and thiobiuret, etc. thereby to form a heavy metal adsorbing resin of this inveition containing a thioureido, thiosemicarbazido, isothiocyanato, thiobiuret, N-thioaminobiuret or N-thiocarbamoyl-polyalkylene polyamino group. This reaction can be performed in the presence of a solvent which can dissolve the sulfur-containing compound, such as water or an alcohol, at room temperature to the reflux temperature. The amount of sulfur-containing compound differs according to the number of amino, hydrazido, or polyalkylene polyamino groups attached to the substrate of the polymer. Generally, it is sufficient to use it in an amount of at least 0.1 in terms of the molar ratio of it as against the amount of the substrate. Specific examples of the sulfur-containing compounds are: the salts of thiocyanic acid such as the lithium, sodium, potassium, magnesium, calcium, strontium, barium or ammonium salt; the thioureas such as thiourea and its alkyl (such as methyl, ethyl or propyl), aryl (such as phenyl), acyl (such as acetyl or benzoyl), or carbamoyl substitution product; and the isothiocyanates such as alkyl (such as methyl, ethyl or propyl) derivatives of isothiocyanic acid or the phenyl or naphthyl derivative thereof.

5. A heavy metal adsorbing resin containing an isothiocyanato group is prepared by going through the stage of a dithiocarbamic acid salt of the above polymer, or by causing thiophosgen to act on the aminated polymer.

6. A polymer of vinyl chloride or vinylidene chloride or a halogenated polymerized type polymer is reacted with thiocyanic acid or thiocyanic acid salt to introduce an isocyanato group.

7. The above isothiocyanato-containing polymer is reacted with a nitrogen-containing compound selected from ammonia, primary and secondary amines, hydrazines and polyamines to produce a heavy metal adsorbing resin containing a thioureido or thiosemicarbazido group. ln this method, the isothiocyanato-containing polymer is reacted with the nitrogen-containing compound at room temperature to the reflux temperature in the presence of an inert solvent which dissolves the nitrogencontaining compound such as water, an alcohol or dimethyl formamide or using the nitrogencontaining compound itself as a solvent. Specific examples of the nitrogen-containing compound used in the above reaction are: the primary amines such as ethylamine or aniline; the secondary amines such as diethyl amine or dipropyl amine: the hydrazine derivatives such as phenyl hydrazine, or hydrazine; and the polyamines such as ethylene diamine, propylene diamine, diethyleneditriamine, triethylene-tetramine or polyethylene imine. Hydrazine and ammonia are especially preferred. The amount of the nitrogen-containing compound used in the reaction may be determined according to the number of isothiocyanate groups attached to the polymer. Usually, it is at least 0.1, preferably at least 0.5, in terms of its molar ratio as against the isothiocyanate groups.

The heavy metal adsorbing resins of this invention are useful for removing and detecting heavy metals upon contact with solutions containing them. When it is desired to remove heavy metals effectively from a solution containing them using the heavy metal adsorbing resin of this invention, it is desirable that the pH of the solution be adjusted to l1l, preferably 3-7, prior to contact with the resin. If the pH of the solution to be treated is less than 1, the amount of the heavy metals to be adsorbed by the resin is reduced. Furthermore, the amount of the heavy metals remaining in the solution after treatment increases, and discharging the solution as such is likely to cause environmental pollution. On the other hand, if the pH of the solution exceeds 9, the heavy metals are converted to their hydroxides, and as a result, the amount of the heavy metals to be adsorbed by the resin decreases.

The method of contacting the heavy metal containing solution with the heavy metal adsorbing resin of this invention is not particularly limited. In commercial practice, it is the practice to pass the solution through a fixed or fluidized bed in which the resin has been packek. Because of the extreme superiority of the resin of this invention in the ability to adsorb heavy metals, it is capable of continuously adsorbing and removing most of the heavy metals until it reaches saturation,

even when a solution containing the heavy metals is treated in a fluidized bed. In addition, since the resin in the fluidized bed adsorbs the heavy metals while being suspended to attain an extremely increased specific gravity, and falls downwards, it is advantageous to employ the up-flow method by which the solution is passed from the bottom and withdrawn from the top.

Advantageously, a solution containing a heavy metal is first treated in a fluidized bed using the heavy metal performed continuously for a prolonged period of time,

. resins used. in this invention are mercury, chromium,

nickel, copper, molybdenum, cobalt, bismuth, manganese, lead, zinc, gold, silver, and platinum. The heavy metal adsorbing resins of this invention especially have the highest ability to adsorb mercury, and is very effective for preventing pollution by mercury since it can adsorb and remove mercury from its solution to a very low concentration. Next in order, the heavy metal adsorbingresinof this invention has a great ability to adsorb gold, silver and platinum, and there can effectively recover these metals from the solutions.

After adsorption of heavy metals, the resin of this invention can be regenerated by simply contacting it with a mineral acid or sodium sulfide or sodium polysulfide to regain its adsorbing ability almost completely. This is surprising in view of the fact that the conventional condensation: type chelate resins cannot be at all regenerated with a mineral acid, and the re-usability of the resin has a very great commercial value.

In order to illustrate the present invention further,

the following Examples and Comparative Examples will be given. However, the present invention is not limited to these Examples. 0

Unless otherwise specified, the measurement of the concentrations of heavy metals in these Examples was performed by thefollowing methods based on JIS K 0102. The concentration of copper was measured by the sodium diethylthiocarbamate method, the concentration of mercury by the flameless atomic absorption -method, the concentration of chromium by the diphenyl carbazide method, the concentration of manganese by the potassium perhydroiodate method, the concentration of bismuth by the bismuth iodide method,

and the concentrations of zinc and lead by the dithizone method. The concentrations of silver and platinum, of which measuring method is not described in JISK 0102, were determined by the dithizone method and the iodoplatinic acid method respectively.

EXAMPLE 1 Hydrazine hydrate cc) was added to 30 g of granules (about 4 0 mesh in size) of polyvinyl chloride, and the mixture was refluxed for 15 hours to form a red resin. Examination of this resin by infrared spectrum shows that an absorption band due to CC, disappeared, and there were an absorption band due to NH and a slight absorption band due to C=CH.

The resin obtained above was converted to its hydrochloride (the resin turned brown), and 20 g of the resin was mixed with 35 g of thiourea and cc of water. The mixture was refluxed for 12 hours to form an orange red resin. Infrared spectrum and elemental analysis showed that this resin contained a thiosemicarbazido group l\lHNHCSNH and a hydrazido group (NHNH The resin so obtained l 1 cc) was packed into a column having an inside diameter of about 1 cm, and a solution of mercury (pH 4.5) having a concentration of 200 ppm, which had been prepared from mercuric chloride, was caused to flow from the top of the column. The concentration of mercury in the solution flowing down from the bottom of the column (to be referred to as the flowthrough value) was measured, and found to be less than 0.001 ppm.

The portion of the resin layer packed in the column which adsorbed mercury turned brown, and there was seen a clear boundary between this portion and the portion which did not adsorb the mercury. This boundary line moved towards the bottom of the column as the amount of the solution passing through the column increased. Accordingly, the suitable time for replacing or regenerating the resin could be easily detected from the change in. the color of the resin layer.

The discolored portion of the resin layer mentioned above was taken out, and the amount of mercury adsorbed to it was measured. It was found that the amount of mercury per unit weight of the resin (to be simply referred to as the adsorption capacity) was 0.51 g per gram of the wet resin. On the other hand, the amount of mercury adsorbed to the undiscolored portion of the resin was 0.0006 g per gram of the wet resin. It is therefore seen that the heavy metal adsorbing resin of this invention has an extremely high rate of adsorbing mercury, and the mercury adsorbed layer is formed orderly.

The volume of a mercury solution with a concentration of 20 ppm which can be treated while maintaining the flow-through value at not more than 0.001 ppm (to be referred to simply as a treating factor) was more than 16,000 cc per cubic centimeter of the resin.

When the resin having adsorbed thereto 0.51 g of mercury per gram of wet resin is regenerated by passing therethrough 6N-hydrochloric acid or lN-sodium sulfide solution. The amount of mercury in the resin was reduced to 3 mg per gram of wet resin, or to 5 mg per gram of wet resin, respectively. This regenerated resin was thoroughly washed with water, and the mercury solution was treated in the same way as above. The adsorption capacity of mercury was again 0.5 g per gram of wet resin.

EXAMPLE 2 (EXAMPLE OF USE) The heavy metal adsorbing resin containing a thiosemicarbazido group produced in Example 1 was packed into a cylindrical packing column having a column diameter of 100 mm, and two-staged fluidized bed (the height of the column was 400 mm in each stage) and one-staged fixed bed (the height of the column was 800 mm) were arranged in series. A mercury solution having a concentration of 200 ppm was introduced into the above packing column at a flow velocity (LV) of 5 meters/hour from the bottom of the fluidized bed, and was passed therethrough while flowing the resin. The aqueous solution which flowed out from the top of the fluidized bed was caused to flow down from the top of the fixed bed. The mercury concentrations (flowthrough value) of the solutions flowing out from the fluidized bed and from the fixed bed were less than 0.008 ppm and 0.001 ppm respectively.

After two-month operation the amount of the treated solution that passed reached about 9,000 times the amount (volume) of the resin in the fluidized bed and it was totally unnecessary to back-wash the resin in the fixed bed.

EXAMPLE 3 Granules of a polystyrene resin (about 25 mesh) were nitrated with a mixed acid, and then reduced with tin and hydrochloric acid to form an aminated polystyrene resin. Ten grams of the aminated polystyrene were mixed with a mixed solution of 27 g of carbon disulfide and 50 cc of concentrated aqueous ammonia, and the mixture was vigorously stirred at room temperature for 5 hours. The product was separated by filtration, and heated to C. to form a black resin.

infrared spectrum and elemental analysis showed that this resin contains a thiourea group (NI-lCSNH An adsorption test on mercury was performed using the heavy metal adsorbing resin obtained above, in the same way as in Example 1. The portion of the resin which adsorbed mercury turned gray black, and there was seen a clear boundary between it and the portion which did not adsorb mercury.

The flow-through value of the resin was less than 0.001 ppm, and the treatment factor was more than 13,000. The adsorption capacity was 0.41 g per gram of wet resin.

The resin was regenerated in the same way as in Example I. When it was treated with 6N-hydrochloric acid, the amount of mercury adsorbed was reduced to 6 mg per gram of wet resin, and when it was treated with lN-sodium sulfide solution, the amount of mercury adsorbed decreased to 8 mg per gram of wet resin.

The same adsorption test on mercury as above was performed using the regenerated resin. The flowthrough value was 0.001 ppm, and the absorption capacity was about 0.4 g per gram of wet resin.

EXAMPLE 4 200 cc of diethylene triamine and cc of water were added to 50 g of granules (about 40 mesh in size) of polyvinyl chloride, and the mixture was refluxed for 12 hours to form a yellow red resin. Infrared spectrum of this product showed that an absorption band due to C--C disappeared and an absorption band due to NH was observed.

Ten grams of this resin was added to a mixed solution of 27 g of carbon disulfide and a solution of 15 g of sodium hydroxide in 32 cc of water, and the mixture was stirred for 3 hours at room temperature. Then, while adding 40 g of ethyl chlorocarbonate dropwise, the mixture was'continuously stirred for 2 hours. infrared spectrum of the resulting resin showed that a strong band due to N=C=S was observed.

l-lydrazine hydrate (30 cc) was added to 10 g of the above resin. With some heating, the mixture was stirred for 2 hours to form an orange red resin. Infrared spectrum of this resin showed that it does not show an absorption band due to N=C=S, and by the infrared spectrum and elemental analysis, the product was identified as containing a thiosemicarbazido group (Nl-1CSNHNH Using the resulting heavy metal absorbing resin, an adsorption test on mercury was performed in the same way'as in Example 1. The portion of the resin which adsorbed mercury turned brown, and was clearly distinguished from the portion which did not adsorb mercury. The flow-through value of the heavy metal adsorbing resin was less than 0.001 ppm, the treatment factor was 18,000, and the amount of mercury adsorbed was 0.52 g per gram of wet resin.

The portion of the resin which adsorbed mercury was regenerated in the same way as in Example 1. When it was treated with 6N-hydrochloric acid, the amount of mercury adsorbed was 4 mg per gram of wet resin. An

9 adsorption test on mercury was performed in the same way as above using the regenerated resin. The amount of mercury adsorbed was about 0.5 g per gram of wet resin.

EXAMPLE (EXAMPLE OF USE) 100 cc of the heavy metal adsorbing resin produced in Example 1 was packed in a column, and each of a silver solution having a concentration of 200 ppm, a gold solution with a concentration of 20 ppm and a platinum solution with a concentration of ppm prepared respectively from silver nitrate, chloroauric acid and chloroplatinic acid was passed through the column in the same way as in Example 1.

The flow-through value of the resin for silver was less 15 EXAMPLE 6 Using each of the resulting resins, an adsorption test on mercury was performed in the same way as in Example 1. The results are shown in Table 1.

Table 1 Results Adsorption capacity Run Functional Flow-through Treatment (g of Hg/g Nos. Base polymers reactants group Value (ppm) factor of wet resin) 1 Aminated polystyr- Phenyl iso -NHCSNph 0.005 10.000 0.33

ene thiocyanate 2 Aminated polystyr- N-ethylthioene urea -NHCSNHEt 0.005 10,000 031 3 An isocyanated Hydrazine -NHCSNHNH less than 11,000 0.38

reaction product 0.001 between chlorinated polypropylene and ammonia 4 A reaction product between polyvinyl Thiobiuret -NHNHCSNH- less than 14,000 0.45 chloride and CONH 0.001 hydrazine 5 A reaction product Acetylthiobetween chlorinated urea -N HNHCSNH- 0.003 10,000 0.30 polyethylene and COCH hydrazine 6 A reaction product between vx/vdc co- Ethyl iso- -NHCSNHEt 0.005 8,000 0.25 polymer and ammonia cyanate 7 A reaction product Ammonium -NHNHCSNH- less than between vc/pr thiocyanate 0.001 15,000 0.49 copolymer and hydrazine 8 A reaction product N-phenylthio -NHNHCSNHph 0.004 12,000 0.37

between pol 'vinyl urea chloride and hydrazine 9 Aminated polystyr- Thiobiuret -NHCSNHCONH less than 12,000 0.38

ene 0.001

10 A reaction product between vo/pr copolymer and N-ethylthio- NHNHCSNHE! 0.005 9.000 0.30 hydrazine urea 1 l A reaction product between chlorinated polyethylene and Acetyl thio- -NHCSN1-1COCH 0.004 10,000 0.30 ethylene diamine urea 12 A reaction product thioures 1 less than between polyvinyl -NHNHCSNH 0.001 15,000 0.45

chloride/polypropylene oxide (2%) graft copolymer and hydrazine 1 Note: In Table I. the vc/vdc copolymer is a copolymer consisting of of vinyl chloride and 70% of vinylidene chloride. the \'c/pr cupolymer is a copolymer consisting 019771 of vinyl choride and 3% of propylene. ph stands for -C,,H,,. and El stands for -C:H,,.

EXAMPLE 7 200 cc of diethylene triamine and 150 cc of water were added to 50 g of granules (about 40 mesh in size) of polyvinyl chloride, and the mixture was refluxed for 12 hours to form a yellow red resin product. Infrared spectrum of the product did not show an absorption band due to CC but showed a strong absorption of NH.

41 grams of ammonium thiocyanate and 200 cc of water were added to 29 g of the hydrochloride of the EXAMPLE 9 Granules of polyvinyl chloride were reacted with triethylene tetramine in the same way as in Example 7, and then with thiourea to form a yellow red resin prodabove resin, and the mixture was heated for 2.5 hours to form a red brown resin product. The ability of the rej sulting resin to adsorb mercury was measured in the The resultmg heavy metal adsorbmg resmswas same way as in Example 1. The flow-through val e was tacted with a solution containing'chromium in a conless than 0.001 ppm. The treatment factor at this flow- Cehtrahoh of 200 PP which was Produced from P through value was more than 16,000 for a mercury so m Chromate- The flow'through Value was about lution with a concentration of 20 ppm ppm. Similarly, the flow-through value was 0.1 ppm for The portion of the resin which adsorbed the mercury pp 2 pp for manganese and 1655 than 5 ppm for turned gray brown, and was clearly distingushed from bismuth. The resin which adsorbed the above heavy the portion which did not adsorb mercury. The amount metals turned light brown. 1 of mercury adsorbed to the discolored portion of the resin was 0.50 g per gram of wet resin. EXAMPLE l0 Furthermore, the ortion of the resin which adsorbed p 100 cc of hydrated hydrazine was added to 30 g of mercury was regenerated using 6N-hydrochlor1c acid or lN-sodium sulfied solution. The amount of mercury granules (about 50 mesh) of polyvmyl chlonde and h adsorbed to the resin was reduced to mg per gram mixture was refluxed for 15 hours to form a red resin of Wet resins Using the regenerated resin, the amount product. Infrared spectrum and elementalanalysis shoof mercury adsorbed was again measured, and found to Wed lh product contalrled a hydrazmo group be 0.5 g per gram of wet resin The ability of the above resin to absorb mercury was measured in the same way as in Example 1. The flow- EXAMPLE 8 through value was 0.02 ppm, and the treatment factor Each of the base polymers shown in Table 2 was rewas more than ZQOOO- acted with each of the reactants indicated in Table 2 by The POTUOn 0f the res!" which adsorbed mercury h same th d as i th previous E l to f turned brown, and was clearly distinguished from the various heavy metal adsorbing resins. portion which did not adsorb mercury (red).

The ability of each of the resulting resins to adsorb The amount of mercury adsorbed to the portion of mercury was measured in the same way as in Example the resin which turned brown was 0.60 g per gram of The sults a h rl in Table wet resin, and the amount of mercury adsorbed to the Table 2 Adsorption capacity reactants Flow- (g of Hg (S-containthrough Treatper gram Run ing comvalue ment of wet Nos. Base polymers pound) (ppm) factor resin) 1 Aminornethylated N-ethyl- 0.005 10,000 0.31

polysturenc thiourea 2 Reaction product Potassium 0.002 10.000 0.32

between chlorinated thiocyanate polypropylene and ethylene diamine 3 Reaction product Thiourea 0.002 11.000 0.36

between aminated polystyrene and polyethylene imine 4 Reaction product Thiobiuret less 14.000 0.45

between polyvinyl than chloride and 0.001 hydrazine 5 Reaction product Calcium 0.005 7.000 0.22

between polyvinyl thiocyanate chloride and piperazine 6 Reaction product Acetyl 0.003 10,000 0.30

between chlorinated thiourea polyethylene and hydrazine The resins based on the aminated polystyrene resin were generally black, and turned gray black on adsorption of mercury. On the other hand, those based on the vinyl chloride resin were generally yellow to red, and

turned brown to light brown on adsorption of mercury.

In both cases, the resins which adsorbed mercury could be clearly distinguished from those which did not.

undiscolored portion of the resin at the bottom of the packing column was only 0.01 g per gram of wet resin.

The resin which was discolored upon adsorption of mercury was regenerated by passing oN-hydrochloric acid and 1Nsodium sulfide solution. In either case, the amount of mercury in the resin decreased to about 10 mg per gram of wet resin. Using the regenerated resin,

the same mercury adsorption test as above was performed. It was founs that the adsorption capacity again showed about 0.60 g per gram of wet resin.

EXAMPLE 1 l The mercury adsorbing ability of each of the resins shown in Table 3 containing the various functional groups shown in Table 3 was tested in the same way as in Example 1. The results are shown in Table 3.

When the regenerated resin was well washed with water and then contacted with the mercury solution in the same manner as above described, the amount of mercury adsorbed again showed 0.5 g per gram of wet .5 resin.

EXAMPLE 14 Polystyrene resin granules (about 15 mesh in size) 1() were nitrated using a mixed acid, and then reduced EXAMPLE l2 (EXAMPLE OF USE) A solution containing copper in a concentration of 200 ppm which was prepared from copper sulfate was passed through the reaction product between a vinyl chloride/propylene copolymer and triethylene tetramine obtained in Example 1 1. The flow-through value for copper was about 1 ppm.

The same adsorption test showed that the flowthrough value for nickel, cobalt and zinc was less than 10 ppm.

EXAMPLE 13 The isothiocyanato-containing resin obtained in Example 4 from polyvinyl chloride granules was immersed in ethanol instead of the hydrazine hydrate used in Example 4, and with some heating, ammonia gas was blown thereinto with stirring. After minutes, a red brown resin was obtained.

The ability of the resulting resin to adsorb mercury was measured in the same way as in Example 1. The flow-through value was less than 0.001 ppm.

The treatment factor of the mercury solution which could be treated while the flow-through value of the resin was maintained at less than 0.001 ppm was more than 16,000 cc.

The portion of the resin which adsorbed mercury turned gray brown, and could be clearly distinguished from the portion which did not adsorb mercury. The

wet resin. The amount of mercury adsorbed to the undiscolored portion of the resin was only 0.004 g per gram of wet resin.

The resin which adsorbed mercury was regenerated by passing 6N-hydrochloric acid and lN-sodium sulfide solution. As a result, the amount of mercury in the resin was reduced to 4-8 mg/g of wet resin in either case.

amount of mercury adsorbed was 0.51 g per gram of I with tin and hydrochloric acid to form aminated polystyrene. Then, in the same way as in Example 13, the aminated polystyrene was reacted with a mixed solution of carbon disulfide and sodium hydroxide. Then, the reaction was performed adding ethyl chloro carbonate. The product was treated with ethanolic ammonia to form a black resin.

The ability of the resulting resin to adsorb mercury was measured in the same way as in Example 1. The flow-through value was less than 0.001 ppm, and the treatment factor at this flow-through value was more than 13,000 cc for the mercury solution having a concentration of 20 ppm.

The resin which adsorbed mercury turned gray black, and could be clearly distinguished from the portion which did not adsorb mercury.

The portionof the resin which discolored upon adsorption of mercury was regenerated using 6N- hydrochloric acid and lN-sodium sulfide solution. In either case, the amount of mercury adsorbed to the resin was reduced to about 8 mg per gram of wet resin. When the regenerated resin was contacted with the mercury solution, the amount of mercury adsorbed to the resin almost returned to the original value.

EXAMPLE 15 Each of the base polymers shown in Table 4 was reacted with a mixed solution of carbon disulfide and sodium hydroxide, and the reaction was continued while adding ethyl chlorocarbonate to form an isothiocyanato-containing resin.

Each of the resulting resins was reacted with each of the reagents shown in Table 4 to form a heavy metal adsorbing resin of this invention. The ability of each of these resins to adsorb mercury was measured in the same way as in Example 1. The results are shown in Table 4.

Table 4 reactants Flow-through Treatment Adsorption Base polymers (N-contuinvalue (ppm) factor capacity ing com- (g of Hg/ pounds) g of wet resin Reaction product Hydrazine less than 1 L000 038 between chlori- 0.001 nated polypropylene and ammonia Reaction product Ethylamine 0.005 9,000 0.27 between polyvinyl chloride and triethylene tetramine Aminated polystyrene Aniline 0.005 10,000 0.33 Reaction product Polyethyl- 0.002 10.000 0.3l between polyvinyl ene imine chloride and ethylene diamine Reaction product Ammonia less than 12.000 0.40 between ammonia 0.001 and a copolymer of vinyl chloride and vinylidene chloride Aminated poly- Phenyl 0.004 l2,00() 0.40 styrene hydrazine Reaction product Acetyl 0.004 10,000 0.30 between chlorinated thiourea polypropylene and ethylene diamine Reaction product between hydrazine and a copolymer of Ammonia less than l5,000 0.49 vinyl chloride/ 0.00l propylene (3%) Aminated Diethyl 0.008 7,000 0.22 polystyrene amine In the above table, the resins based on the aminated Table 5 polystyrene were generally black, and turned gray Concentration of black on adsorption of mercury. On the other hand, those which were based on the vinyl chloride resin were generally yellow to red, and turned brown to light brown on adsorption of mercury. In either case, the change in color was very distinct.

EXAMPLE l6 (EXAMPLE OF USE) The heavy metal adsorbing resin obtained in Example 4 was packed into a column in the same way as in Example 1, and a chromium solution containing chromium in a concentration of 200 ppm which was prepared from potassium chromate was passed through the column. The flow-through value of the resin was less than 0.1 ppm.

The same test was conducted on copper, manganess and bismuth and it was found that the flow-through value was 0.1 ppm for copper, 2 ppm for manganese and less than 5 ppm for bismuth.

When the heavy metal adsorbing resins obtained in Examples 15 and 16 were used, similar results to those shown above were obtained.

EXAMPLE l7 (EXAMPLE OF USE) Five grams each of the resin obtained in Example 1 was added to a solution containing mercury in a concentration of 1000 ppm which had been prepared from mercuric chloride (Hgcl and then adjusted to the desired pH value using a buffer solution. Each of the mixtures obtained was stirred for 4 hours.

The concentration of mercury remaining in the solution was analyzed. The results are shown in Table 5 below.

PH of the mercury remaining mercury EXAMPLE l8 (EXAMPLE OF USE) Two packing columns having a column diameter of mm were used. In one (first column) of them, the hydrazino-containing adsorbing resin obtained in Example 10 was packed, and in the other (second column), the thiosemicarbazido-containing adsorbing resin obtained in Example 1 was packed. The first and second columns were joined with a pipe, and a mercury solution containing mercury in a concentration of 20 ppm and adjusted to a pH 4-5 was introduced from the top of the first column. The solution which flowed out from the bottom of the first column was led to the top of the second column, and finally withdrawn from the bottom of the second column.

The amounts of mercury contained in the solution withdrawn from the bottoms of the first and second columns were less than 0.02 ppm and 0.001 ppm, respectively.

COMPARATIVE EXAMPLE 1 The ability of the commercially available condensation type chelate resin comprising resorcinolformaldehydethiourea (MA Resin, product of Hokuetsu Car- 17 bon Co. Ltd.) to adsorb mercury was measured in the same way as in Example 1. The adsorption capacity was 0.1 l g per gram of wet resin. The flow-through value was 0.001 ppm. and the treatment factor of a mercury solution containing mercury in a concentrationof 20 ppm was only 1,500 cc at this flow-through value. The change in color of the resin by adsorption of mercury was not distinct.

What we claim is: l. A heavy metal adsorbing resin consisting essentially of a polymer comprising:

A. a backbone polymer selected from polystyrene, polyvinyl chloride, a copolymer of vinyl chloride with another copolymerizable monomer, a graft 

1. A HEAVY METAL ADSORBING RESIN CONSISTING ESSENTIALLY OF A POLMER COMPRISING: A. A BACKBONE POLYMER SELECTED FROM POLYSTYRENE, POLYVINYL CHLORIDE, A COPOLYMER OF VINYL CHLORIDE WITH ANOTHER COPOLYMERIZABLE MONOMER, A GRAFT COPOLYMER OF A RUBBERY SUBSTANCE TO WHICH VINYL CHLORIDE HAS BEEN GRAFTED AND A CHLORINATED POLYOLEFIN, AND B. A MOIETY ATTACHED TO THE BACKBONE POLYMER WHICH IS SELECTED FROM THE N-THIOCARBAMOYL-POLYALKYLENE POLYAMINE GROUP CONSISTING OF-NH(CH2CH2NH)NCSNHR, WHEREIN R IS A HYDROGEN ATOM-ALKYL MOIETY, ARYL MOIETY, OR ACYL MOIETY, AND N IS FROM 1 TO
 100. 2. The resin of claim 1 wherein said polymer contains at least one said functional group per about 250 monomer units. 